FIBER AND CONCRETE ADDITIVES

CIS CHEM UYK 7314

HIGH INTENSITY COPOLYMER GLASS FIBER
PRODUCTCATEGORY: GLASS FIBER

Product Discription

CIS CHEM UYK 7314 is a high flow, halogen free flame retardant, copolymer reinforced with 20% long glass fiber, developed for Injection molded applications. This material has been designed to combine a good performance profile with good processing. CIS CHEM UYK 7314 should be dried at 100C for 2 hours before the injection molding. Melt temperature of 240 °C should not be exceeded during processing.

Application

• CIS CHEM UYK 7314 into concrete or mortar, could effectively prevent temperature change
• and Micro-crack which is caused by plastic and dry shrinkage
• Projects like concrete road, bridge, airport road and factory floor which strictly require cracking resistance
• They are widely used in roads, bridges, underground waterproof projects and roof, walls
• pools, basements of civil construction industrial

---

Storage

To be stored in its closed original package,keep cool and dry, avoid humidity

---

Packaging

25kg plastic bag 600grams*40bags inner. ( 1 kg extra)

---

Specification

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
POLYMER PROPERTIES
Density	1225	kg/m³	ISO 1183
Glass fibre content	20	%	ISO3451
MECHANICAL PROPERTIES
Tensile modulus
at 23 °C	6000	Mpa	ISO 527/1A
at 80 °C	2900	Mpa	ISO 527/1A
Tensile strength
at 23 °C	70	Mpa	ISO527/1A
at 80 °C	37	Mpa	ISO527/1A
Tensile strength
at 23 °C	2.1%		ISO527/1A
Flexural Modulus
at 23 °C	6200	Mpa	ISO 178
at 80 °C	4000	Mpa	ISO 178

---